Pengaruh Variasi Temperatur Kalsinasi Terhadap Sifat Kapasitif Kapasitor Elektrokimia Tungsten Trioksida (Wo3) Hasil Sintesa Sol Gel

Augus Tino Tri Widyantoro, Diah Susanti
Submission Date: 2013-01-30 13:18:46
Accepted Date: 2013-03-01 00:00:00

Abstract


Kapasitor elektrokimia mampu menjembatani kinerja kritis antara kapasitor konvensional dan baterai. Densitas energi kapasitor elektrokimia ratusan kali lebih besar daripada kapasitor konvensional sedangkan densitas dayanya ribuan kali lebih besar daripada baterai. Penelitian ini bertujuan untuk mempersiapkan material WO3 sebagai kapasitor elektrokimia.Material tungsten trioksida (WO3) dapat disintesa dari tungsten(VI) heksaklorida (WCl6) denganĀ  metode sol-gel dan kalsinasi. WO3 hasil sintesa tersebut dilapiskan pada substrat grafit kemudian dikalsinasi dengan variasi temperatur 300oC, 400oC, 500oC dan 600oC selama waktu tahan 1 jam. Dari hasil uji XRD diketahui struktur kristal WO3 temperatur kalsinasi 300oC adalah orthorombik sedangkan WO3 temperatur kalsinasi 400oC, 500oC dan 600oC adalah monoklinik. Dari hasil uji SEM didapatkan ukuran partikel yang semakin besar seiring kenaikan temperatur kalsinasi. Dari uji BET didapatkan luas permukaan aktif WO3 yang semakin kecil seiring kenaikan temperatur kalsinasi. Dari uji CV dihasilkan nilai kapasitif terbesar terdapat pada WO3 temperatur kalsinasi 300oC scan rate 2 mV/s yaitu sebesar 5991 mF/gr. Hal ini diperkuat dari hasil uji EIS yang menunjukkan bahwa WO3 temperatur kalsinasi 300oC memiliki nilai impedansi paling kecil sehingga sifat kapasitifnya paling baik.


Keywords


Kapasitor Elektrokimia; Tungsten Trioksida (WO3); Sol-gel; Kalsinasi; Cyclic Voltametri (CV); electrochemical impedance spectroscopy (EIS)

Full Text: PDF

CC Licencing


Authors who publish with this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).

Refbacks

  • There are currently no refbacks.


Creative Commons License
Jurnal Teknik ITS by Lembaga Penelitian dan Pengabdian Kepada Masyarakat, LPPM-ITS is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Based on a work at https://ejurnal.its.ac.id/index.php/teknik.
Statistik Pengunjung