Pengaruh Konsentrasi Karbon Terhadap Performa Elektrokimia Katoda Lifepo4 Untuk Aplikasi Baterai Lithium Ion Tipe Aqueous Electrolyte

Abstract

Baterai lithium ion rechargeable telah dipertimbangkan sebagai sebuah sumber tenaga listrik yang digunakan untuk berbagai aplikasi. LiFePO4 yang digunakan sebagai katoda, dipilih karena memiliki sifat yang ramah lingkungan tetapi memiliki konduktivitas yang lemah. LiFePO4 dilakukan proses konduktif coating menggunakan sukrosa dengan pemanasan 600oC selama 3 jam didalam atmosfer argon untuk membentuk karbon coating LiFePO4 (LiFePO4/C) dengan variasi persentase berat karbon 9%, 14.5%, dan 17.8% karbon. Dari analisis cyclic voltammetry penambahan karbon coating dapat meningkatkan stabilitas didalam aqueous electrolyte. Hasil galvanostatic charge/discharge didapatkan hasil terbaik pada LiFePO4/C dengan persentase berat karbon 9% dengan kapasitas discharge 13.3 mAhg-1 dan mengalami penurunan kapasitas sebesar 2.2% setelah cycle ke 100. Penambahan karbon yang berlebihan menurunkan kapasitas LiFePO4

CC Licencing

Authors who publish with this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).