Sintesis MgTiO3 dengan Variasi Temperatur Kalsinasi Menggunakan Metode Pencampuran Larutan

Riyan Angela, Suminar Pratapa
Submission Date: 2012-07-25 12:31:23
Accepted Date: 2013-01-17 08:28:08

Abstract


Telah dilakukan sintesis MT (magnesium titanat) dengan metode pencampuran larutan. Prekursor dibuat dengan melarutkan serbuk logam ke dalam HCl 37% dan dikeringkan di udara pada temperatur 110oC dilanjutkan dengan kalsinasi. Dalam penelitian ini digunakan variasi temperatur kalsinasi yaitu 600°C, 700°C, 800°C dengan waktu tahan yaitu 1 jam untuk mengetahui pengaruhnya terhadap sintesis MT. Hasil sintesis dikarakterisasi dengan XRD (X-Ray Diffraction), kemudian dianalisis menggunakan software rietica dan MAUD. Hasil analisis menunjukkan bahwa temperatur dan waktu tahan kalsinasi mempengaruhi hasil dari sintesis. Berdasarkan metode Rietveld untuk fraksi berat relatif komposisi fase, pembentukan MT  yang paling optimal adalah pada temperatur 800 oC,waktu tahan 1 jam dengan fraksi berat 95,1%. Dengan analisis menggunakan MAUD diperoleh nanokristal MgTiO3 pada pemanasan 600oCdengan ukuran kristal 75nm.


Keywords


magnesium titanat; metode pencampuran larutan; temperatur kalsinasi; waktu tahan; nanokristal

Full Text: PDF

CC Licencing


Authors who publish with this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).

Refbacks

  • There are currently no refbacks.


Lembaga Penjaminan Mutu, Pengelolaan dan Perlindungan Kekayaan Intelektual (LPMP2KI) ITS
Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.